In undoped lead zirconate titanate films of 1–2  μm thick, domain walls move in clusters with a correlation length of approximately 0.5–2  μm. Band excitation piezoresponse force microscopy mapping of the piezoelectric nonlinearity revealed that niobium (Nb) doping increases the average concentration or mobility of domain walls without changing the cluster area of correlated domain wall motion. In contrast, manganese (Mn) doping reduces the contribution of mobile domain walls to the dielectric and piezoelectric responses without changing the cluster area for correlated motion. In both Nb and Mn doped films, the cluster area increases and the cluster density drops as the film thickness increases from 250 to 1250 nm. This is evident in spatial maps generated from the analysis of irreversible to reversible ratios of the Rayleigh coefficients. 

While hexagonal boron nitride (hBN) has been widely used as a buffer or encapsulation layer for emerging electronic devices, interest in utilizing it for large‐area chemical barrier coating has somewhat faded. A chemical vapor deposition process is reported here for the conformal growth of hBN on large surfaces of various alloys and steels, regardless of their complex shapes. In contrast to the previously reported very limited protection by hBN against corrosion and oxidation, protection of steels against 10% HCl and oxidation resistance at 850 °C in air is demonstrated. Furthermore, an order of magnitude reduction in the friction coefficient of the hBN coated steels is shown. The growth mechanism is revealed in experiments on thin metal films, where the tunable growth of single‐crystal hBN with a selected number of layers is demonstrated. The key distinction of the process is the use of N₂gas, which gets activated exclusively on the catalyst's surface and eliminates adverse gas‐phase reactions. This rate‐limiting step allowed independent control of activated nitrogen along with boron coming from a solid source (like elemental boron). Using abundant and benign precursors, this approach can be readily adopted for large‐scale hBN synthesis in applications where cost, production volume, and process safety are essential.